6061 T6 aluminum flat bar is a heat-treatable alloy with good formability, weldability, machinability, moderate strength and annealed
The main alloying elements of 6061 T6 aluminum flat bar are magnesium and silicon, which form Mg2Si phase.If it contains a certain amount of manganese and chromium,
Can neutralize the bad effects of iron;Sometimes a small amount of copper or zinc is added to enhance the strength of the alloy without significantly reducing its corrosion resistance.
There is also a small amount of copper in the conductive material to offset the bad effects of titanium and iron on the conductivity;Zirconium or titanium can refine grain and control recrystallization structure.
In order to improve the machinability, lead and bismuth can be added.In Mg2Si solid dissolved in aluminum, the alloy has the function of artificial aging hardening.
PRODUCT PARAMETERS 6061 T6 aluminum flat bar
| alloy | 6061 T6 aluminum flat bar |
| temper | O, T4, T6, T651 |
| thickness（mm） | 3-100 |
| width（mm） | 5-100 |
| length（mm） | 500-6000 |
| application |
|
| alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Zr | others | AL | ||
| New brand | Old brand | 0.40-0.80 | 0.70 | 0.15-0.40 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | —— | each | total | |
| 6061 | LD30 | 0.05 | 0.15 | remain | |||||||||
| Alloy with temper |
Tensile Strength Rm/Mpa |
Extension Strength Rp0.2/Mpa |
Elongation/% | hardness/ HBWα |
| 6061-T6 | 290 | 240 | 10 | 95 |
| Alloy with temper |
coefficient of thermal expansion (20-100℃) μm/m·k Rm/Mpa |
Melting point range (℃) Rp0.2/Mpa |
conductivity 20℃(68℉) (%IACS) |
specific resistance 20℃(68℉) Ωmm2/m |
density (20℃)(g/cm3) Ωmm2/m |
| 6061-T6 | 23.6 | 582-652 | 40 | 0.043 |
2.8 |